Intergranular Corrosion Instrument Sensitization Test-a Method Kit

Intergranular corrosion is a kind of local corrosion of metals, which usually occurs in stainless steel, aluminum alloy, brass and nickel base alloy. crystal
Intergranular corrosion is the corrosion extending inward along the boundary between metal grains. The reason of intergranular corrosion is the chemical formation between the surface and interior of grains
And the existence of grain boundary 

The electric heater is directly put into the lower part of hydrochloric acid solution, with uniform heating and high efficiency

1. The concentration of hydrochloric acid used in electrolytic acid etching method is only half of that of thermal acid etching method, and there is no need of heating, low temperature and less volatilization of hydrochloric acid, which significantly improves the working environment.
2. The device does not need to be preheated. Turn on the power supply to corrode and save time; Multiple rows of sa

Pch-1000 sample fixture for controlling grinding and polishing quantity is mainly used to control the thickness of metallographic samples during grinding and polishing
The observed position is on the sample surface

-High resolution image sensor is adopted, with good color restoration and high definition
-1 / 2.5 inch progressive image sensor, hardware 5 megapixels
-The brightness, contrast, saturation, sharpness and gamma value can be adjusted by software
-Automatic white balance, automatic exposure
-Use of USB2.0 high speed interface
-Support Microsoft Windows XP / Vista / 7 / 8 / 10 (32 & 64 bit), OS X

PLC and thyristor are used to control the thermal acid etching process of macrostructure, the heating temperature is controlled more accurately, and the volatilization of hydrochloric acid is reduced to the minimum, so as to significantly improve the working environment;
Automatic liquid level detection, alarm and automatic power off to effectively prevent dry burning;
Separate sediment filter pla

Eqm-3000 series end quenching testing machine meets the requirements of GB / t225-2006Astma255, din50191, iso642 "end of steel hardenability"
Quenching test method (Jominy test) ". Suitable for high quality carbon
Hardenability of alloy structural steel, spring steel, tool steel, bearing steel, etc
Can test.

Eqm-2000 series end quenching testing machine meets GB / t225-2006, ASTM A 255, DIN 50191 and ISO 642 "end quenching test method for steel hardenability (Jominy test)". It is applicable to the hardenability test of high-quality carbon, alloy structural steel, spring steel, tool steel, bearing steel and other steel grades.